Quality inspection of oxide film after anodization of aluminum and its alloys
1 The surface of the parts after anodizing of aluminum alloy should have a uniform oxide film. The color of the oxide film is different due to the difference of aluminum alloy composition, oxidation treatment method and sealing treatment method. Except for the fixture printing on the entire oxidized surface, no defects such as scratches, crushing, scratches, electric burns, local corrosion and oxide film cracks of the unoxidized part or the destruction of the oxide film are allowed, or with fingers A loose oxide film that can be rubbed off by friction.

2 The colorless oxide film anodized by sulfuric acid does not allow: other mottled colors, or surface blooming, blackening, dark lines, etc. due to poor surface preparation, or defects caused by poor sealing. The oxidized anodized film of sulfuric acid should be orange-yellow after being blocked by potassium dichromate. It is not allowed to have a white and light color due to poor sealing. The colored oxide film should be brightly colored and meet the requirements of the dyeing sample. Do not allow: bright spots, dark spots, uneven color.

3 Oxalic acid anodized film has different thickness depending on the type of current used, and the surface is yellow-green to dark brown.

4 The chromic acid anodized film generally consists of gray to grayish black, and is not allowed to have: yellow spots, white spots, redness and blackening of the local film layer.

专栏:Industry information
作者: 佚名
原文链接: 阅读原文
上一页:The difference between electrolytic polishing and chemical polishing of aluminum alloy
下一页:Who is stronger with aluminum anodizing and chemical oxidation?